Processing induced the variation of amorphous ratio, PL quenching, and the exciton nonradiative decay in neat IT-4F films. Here, 0-RT indicates that the film was processed without SAA at room temperature, 0.5, 1, and 1.5 indicate the increase in SAA molar ratio. T80, T120, and T160 mean that the film was post-annealed at 80 °C, 120 °C, and 160 °C respectively.